I-alumina emhlophe edityanisiweyo yi-alumina engumgubo njengento ekrwada, rhoqo ngaphezu kwe-2000 ℃ ubushushu obuphezulu obunyibilikisa isithando sombane se-arc, emva kokutyumza iplastiki, ukwahlukana kwamagnetic kwintsimbi, isikrini sahlulwe saziintlobo ngeentlobo zobungakanani bamasuntswana, ubume obuxineneyo, ubulukhuni obuphezulu, i-granular form Angle hardness. iphezulu kune-alumina emdaka edityanisiweyo incinci, ubulukhuni obusezantsi kancinane, amandla okusika awomeleleyo kunye nokuzinza kweekhemikhali kulungile, inokwaleka okuhle kakhulu.
I-alumina edibeneyo emhlophe yenziwe nge-high-purity low-sodium alumina powder ngokunyibilika kwiqondo lobushushu eliphezulu, ukupholisa icrystallization, emva koko ukutyumza.Igrit ye-alumina edityanisiweyo emhlophe iphantsi kolawulo olungqongqo ukugcina ubungakanani bokuhanjiswa kweenkozo kunye nenkangeleko engaguqukiyo.
Ngokuqhelekileyo isetyenziswe kwi-ladle castables, izixhobo ze-iron runer, izixhobo zokuxuba i-refractory gunning kunye nezinye iimveliso ze-monolithic refractory;
Kwizinto ezibunjiweyo zokuchasa, isetyenziswa ikakhulu kwizinto ezikumgangatho ophezulu kwizitena ze-corundum, i-corundum mullite, ukucokisa izitena zeplagi zentsimbi, i-spray gun, i-steelmaking kunye neshishini eliqhubekayo lokuphosa.
Isenokusetyenziswa njengezixhobo zokupholisha, ukuphosa ngokuchanekileyo, ukutshiza kunye nokugquma, iiseramikhi ezikhethekileyo
Imhlophe, i-crystal α ngaphezu kwe-99%, ubunyulu obuphezulu, ubunzima obuphezulu, kunye nokuqina okuphezulu, amandla okusika anamandla, ukuzinza okuqinileyo kweekhemikhali, kunye nokugquma okuqinileyo.
Mohs ubulukhuni | 9 |
Unizi lolwapho kuyiwa khona | 1.75-1.95g/cm3 |
Ubunzima obuthile | 3.95g/cm3 |
Ukuxinana komthamo | 3.6 |
Idigri yokunyibilika | 2250℃ |
Idigri yeRefractory | 2000℃ |
Iipropati | 0-1 1-3 3-5m/m | F100 F200 F325 | |||
Ixabiso lesiqinisekiso | Ixabiso eliqhelekileyo | Ixabiso lesiqinisekiso | Ixabiso eliqhelekileyo | ||
Ukuqulunqwa kwemichiza | Al2O3 | ≥99.1 | 99.5 | ≥98.5 | 99 |
SiO2 | ≤0.4 | 0.06 | ≤0.30 | 0.08 | |
Fe2O3 | ≤0.2 | 0.04 | ≤0.20 | 0.1 | |
Na2O | ≤0.4 | 0.3 | ≤0.40 | 0.35 |
Uhlobo lweePropati | Iinkozo | ||
8# 10# 12# 14# 16# 20# 22# 24# 30# 36# 40# 46# 54# 60# 70# 80# 90# 100# 120# 150# 180# 220# | |||
Ixabiso lesiqinisekiso | Ixabiso eliqhelekileyo | ||
Ukuqulunqwa kwemichiza | Al2O3 | ≥99.1 | 99.5 |
SiO2 | ≤0.2 | 0.04 | |
Fe2O3 | ≤0.2 | 0.03 | |
Na2O | ≤0.30 | 0.2 |
Uhlobo lweePropati | I-Micropowder | |||
“W” | W63 W50 W40 W28 W20 W14 W10 W7 W5 W3.5 W2.5 W1.5 W0.5 | |||
"FEPA" | F230 F240 F280 F320 F360 F400 F500 F600 F800 F1000 F1200 F1500 F2000 | |||
"JIS" | 240# 280# 320# 360# 400# 500# 600# 700# 800# 1000# 1200# 1500# 2000# 2500# 3000# 4000# 6000#050#1020 | |||
Ixabiso lesiqinisekiso | Ixabiso eliqhelekileyo | |||
Ukuqulunqwa kwemichiza | Al2O3 | ≥99.1 | 99.3 | |
SiO2 | ≤0.4 | 0.08 | ||
Fe2O3 | ≤0.2 | 0.03 | ||
Na2O | ≤0.4 | 0.25 |
1.Akukho mpembelelo malunga nombala weendawo ezicutshungulwayo.
I-2.Ingasetyenziselwa kwiinkqubo apho i-residu ye-iron powder inqatshelwe ngokungqongqo.
3.Ukubunjwa kweenkozo zifaneleke kakhulu kwi-sandblasting emanzi kunye nemisebenzi yokupolisha.
1.Ukuqhunyiswa kwesanti, ukupolisha kunye nokusila isinyithi kunye neglasi.
2. Ukuzaliswa kwepeyinti, i-coating-resistant coating, i-ceramic, kunye ne-glaze.
3.Ukwenziwa kwevili lokusila, i-sandpaper kunye nelaphu le-emery.
4.Ukuveliswa kweembrane zokucoca i-ceramic, iibhubhu ze-ceramic, iiplate ze-ceramic.
5.Ukusetyenziswa komgangatho ongagungqiyo.
6.I-Sandblasting yeebhodi zeesekethe.
7.I-Sandblasting yeenqanawa, iinjini zeenqwelo-moya, imizila kaloliwe kunye nemizimba yangaphandle.
Iinkozo ze-aluminiyam oxide 8.Ezihlukeneyo ezimhlophe ezidityanisiweyo zinokuveliswa ngokweemfuno ezahlukeneyo zabathengi.
Ukuba unayo nayiphi na imibuzo.Nceda uzive ukhululekile ukuqhagamshelana nathi.